SINTESIS DAN KARAKTERISASI TERMAL PLASTIK RAMAH LINGKUNGAN POLYBLEND SELULOSA AMPAS TEBU DAN LIMBAH BOTOL PLASTIK POLIETILEN TEREFTALAT
Abstract
Telah dilakukan penelitian mengenai polyblend dari selulosa ampas tebu dan limbah botol plastik polietilen tereftalat (PET) dalam pembuatan plastik ramah lingkungan. Tujuan penelitian ini adalah untuk mengetahui karakteristik plastik poliblend PET-selulosa dan stabilitasnya secara termal. Hasil analisis FTIR selulosa dan PET menunjukkan adanya gugus fungsi -OH streching pada selulosa pada bilangan gelombang 3328,08 cm-1. Sedangkan pada PET menunjukkan adanya gugus fungsi CH2 alkana pada bilangan gelombang 2984,63 cm-1. Setelah dilakukan pembuatan poliblend plastik ramah lingkungan dengan beberapa variasi menunjukkan bahwa variasi 50/50 merupakan perbandingan yang paling baik dalam pembuatan poliblend plastik ramah lingkungan antara PET dan selulosa. Hal tersebut dapat dilihat dari hasil analisis DTA-TGA menunjukkan bahwa variasi 50/50 paling stabil secara termal.
Kata kunci: poliblend, PET, selulosa
Published
Issue
Section
License
Authors who publish with this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).