Karakterisasi Pengaruh Orientasi Serat terhadap Sifat Mekanis dan Fisis Komposit Serat Tandan Kosong Kelapa Sawit
Abstract
The use of fiber as an amplifier in polymer composite material products has increased in recent years. The advantages owned by fiber empty palm oil are price is cheap, low density, a very large amount, and eco-friendly. The study utilized palm oil empty group fibers (TKKS) to produce filler material and yukalac resin 157 BQTN into its binding matrices and mepoxe catalysts as resin hardeners. Previous research on polyester resins strengthened with fibers in the form of TKKS fibers using variations in the orientation of straight, random, and woven fibers and TKKS was given a 5% NaCl soaking variation treatment without treatment, soaking 2 hours and 4 hours. Researchers have conducted physic tests, namely density tests aimed at finding out the orientation of fibers and the length of NaCl treatment of TKKS composite strength. The best strength of Density test is the orientation of woven fiber without immersion nacl of 1,178 gr / cm3 and the lowest strength is random without treatment NaCl is 1,067 gr / cm3.
Keywords: Waste TKKS, NaCl, Physic Test, Composite.
References
Indonesia Investments (2017). Agriculture Commoditiy Watch Indonesia: Crude Palm Oil. Dikutip 19 April 2019 dari Agriculture Commoditiy Watch Indonesia: Crude Palm Oil: (https://www.indonesia-investments.com/id/news/todays-headlines/agriculture-commodity-watch-indonesia-crude-palm-oil/item7864?)
Hendaryati, D.D dan Arianto, Yanuar, 2017. Statistik Perkebunan Indonesia. Sekretariat Direktorat Jenderal Perkebunan. Kementrian Pertanian. Indonesia. Dikutip 19 April 2019 dari Statistik Perkebunan Indonesia: (https://www.google.com/search?q=Hendaryati%2C+D.D+dan+Arianto%2C+Yanuar%2C+2017.+Statistik+Perkebunan+Indonesia.+Sekretariat+Direktorat+Jenderal+Perkebunan.+Kementrian+Pertanian.+Indonesia.&oq=Hendaryati%2C+D.D+dan+Arianto%2C+Yanuar%2C+2017.+Statistik+Perkebunan+Indonesia.+Sekretariat+Direktorat+Jenderal+Perkebunan.+Kementrian+Pertanian.+Indonesia.&aqs=chrome..69i57.2765j0j7&sourceid=chrome&ie=UTF-8)
Haryanti, dkk, 2014. Studi Pemanfaatan Limbah Padat Kelapa Sawit. Jurnal Teknik Kimia. Volume 3 No. 2. Universitas Mulawarman: Samarinda.
Leody, I.P. 2016. Analisis Komposit Dengan Penguat Serat Rami 40% Dan Serbuk Kayu Sengon 60% Pada Fraksi Volume 40%, 50%, 60% Bermatrik Resin Polyester Untuk Panel Akuistik. Skripsi. Tidak diterbitkan Fakultas Teknik Universitas Muhammadiyah: Surakarta.
Kaw A.K., Mechanics of Composite materials, CRC Press, New York. 1997.
Diharjo, Kuncoro, 2006. Pengaruh Perlakuan Terhadap Sifat Tarik Bahan Komposit Serat Rami-Polyester. Jurnal Teknik Mesin Fakultas Teknik Universitas Negeri Sebelas Maret.
Porwanto, D.A dan Johar Lizda, 2009. Karakterisasi Komposit Berpenguat Serat Bambu Dan Serat Gelas Sebagai Alternatif Bahan Baku Industri. Jurnal Teknik Fisika Institut Teknik Sepuluh November: Surabaya
Bagir, Achmad dan Perdana, G.K 2011. Pemanfaatan Serat Eceng Gondok Sebagai Bahan Baku Pembuatan Komposit. Jurnal Teknik Kimia Fakultas Teknik Universitas Diponegoro: Semarang.
Purboputro, P.I, 2006. Pengaruh Panjang Serat Terhadap Kekuatan IMPak Komposit Eceng Gondok Dengan Matriks Poliester. Jurusan Teknik Mesin Universitas Muhammadiyah: Surabaya.
Pratama, Y.Y, dkk, 2014. Pengaruh Perlakuan, Fraksi Volume Serat, Dan Panjang Serat Terhadap Kekuatan Tarik Komposit Serat Sabut Kelapa-Polyester. Jurusan Teknik Industri Universitas Sebelas Maret: Surakarta.
Agustin Lya, dkk, 2016. Karakteristik Serat Tandan Kosong Kelapa Sawit (TKKS) Dengan Perlakuan Perebusan Dan Pengukusan. Jurnal Teknik Mesin Volume 41 No. 1. Universitas Lambung Mangkurat: Banjarmasin.
Sriwita, Delni dan Astuti, 2014. Pembuatan Dan Karakterisasi Sifat Mekanik Bahan Komposit Serat Daun Nanas-Polyester Ditinjau Dari Fraksi Massa Dan Orientasi Serat. Jurnal Fisika Unand Vol. 3, No. 1. Universitas Andalas Kampus Unand, Limau Manis: Padang.
Devriana, R.P, 2017. Karakteristik Komposit Berpenguat Serat Tandan Kosong Kelapa Sawit Dengan Komposisi Fraksi Volume Serat 4%, 6% dan 8% Menggunakan Perlakuan Curing. Skripsi. Tidak diterbitkan. Fakultas Sains Dan Teknologi Universitas Sanata Dharma: Yogyakarta.
Wibisono, D, 2007. Pegaruh Perendaman Larutan Alkali Serat Widuri Terhadap Sifat Fisis Dan Mekanis Komposit Dengan Matrik Poliester. Skripsi. Tidak diterbitkan. Fakultas Sains Dan Teknologi Universitas Sanata Dharma: Yogyakarta.