Pengaruh Hasil Pengelasan Model Smaw Terhadap Kekuatan Tarik Baja ST 37 Dan ASTM A36
Keywords:
Shielding Metal Arc Welding (SMAW), Metode Taguchi, Analisis Of Variance (ANOVA)Abstract
ABSTRACT
The development of an increasingly advanced manufacturing industry cannot be separated from welding because it has an important role in metal engineering and repair. This research was conducted using a tensile testing technique. The materials used are ST37 and ASTM A36 steel plates, the use of these materials is due to their applications, starting from bolts, vehicle bodies to basic construction. The purpose of this research is to obtain the parameters that affect the welding process so as to obtain products with better quality. For the research method using the Taguchi method, namely the signal to noise ratio (S/N) and orthogonal arrays with the ANOVA analysis method. The best combination of welding on ST37 and ASTM A36 materials is with a current strength of 110 A, electrode type E7016, and a welding position of 2G. Furthermore, from the combination obtained, a tensile test was carried out again, the stress value was obtained which was not much different from the previous nine tests. Based on the results of the ANOVA calculation, there is a significant difference in the welding parameter factors that affect the tensile strength value. The conclusion of this study is that the welding parameter settings for the ST 37 material with the highest tensile stress value are 300.29 MPa and the S/N Ratio value is 49.55. The ASTM A36 material obtained the largest tensile test value of 319.98 MPa and a S/N Ratio value of 50.10. The most influential parameter for both materials is the current parameter (amperes).
References
Mohruni, A. S., & Kembaren, B. H. (2018). Pengaruh Variasi Kecepatan dan Kuat Arus Terhadap Kekerasan, Tegangan Tarik, Struktur Mikro Baja Karbon Rendah dengan Elektroda E6013. Jurnal Rekayasa Mesin, Vol. 13(1).
Saputra, Adhie. (2021). Pengaruh Ampere terhadap Cacat Las pada Pengelasan Baja Lunak dengan Menggunakan Pengelasan SMAW Posisi Pengelasan 2F. Laporan Tugas Akhir Teknik Mesin: Polman Babel.
Bakhori, Ahmad. (2017). Perbaikan Metode Pengelasan SMAW (Shield Metal Arc Welding) pada Industri Kecil di Kota Medan. Jurnal Buletin Utama Teknik, Vol 13(1).
Amin. A. (2017). Pengaruh Variasi Arus Listrik Terhadap Kekuatan Tarik Dan Struktur Mikro Sambungan Las Titik (Spot Welding) Logam Dissimilar Stainless Steel Dan Baja Karbon Rendah. Jurnal Ilmiah Teknik Mesin, Vol 2(1).
Anwar, B. (2017). Analisis Kekuatan Tarik Hasil Pengelasan Posisi Bawah Tangan dengan Perbedaan Variasi Kuat Arus Listrik pada Baja ST.42. Jurnal Teknologi, Vol 16(1).
Rio Rinaldi, dkk. (2019). Studi Eksperimental Kekuatan Tarik dan Kekerasan pada Sambungan Pipa ASTM A 106 Grade B dengan pengelasan SMAW. Journal of Welding Technologi.
Rizki Wahyudi, dkk. (2019). Analisa Pengaruh Jenis Elektroda pada Pengelasan SMAW Penyambungan Baja Karbon Rendah dengan Baja Karbon Sedang terhadap Tensile Strenght. Journal of Welding Technologi.
Sujit Jhumar. (2017). Parametric Optimization of Turning Process Using Taguchi Method and ANOVA Analysis International. Journal of Advances in Engineering & Technology (IJAET).
Suryono, dkk. (2020). Analisa Uji Tarik Las SMAW Terhadap Sambungan Square Butt Joint Dengan Variasi Ketebalan Plat ST 37. Jurnal Teknika.
Agustiawan, R dan Imran. (2018). Analisa Besar Arus Pengelasan terhadap Kekuatan Tarik dan Kekerasan pada Sambungan Plat Baja Karbon ST 40 dengan Menggunakan Pengelasan SMAW. Seminar Nasional Industri dan Teknologi (SNIT), Politeknik Negeri Bengkalis.
Putri, F. (2018). Analisa Pengaruh Variasi Kuat Arus Dan Jarak Pengelasan Terhadap Kekuatan Tarik, Sambungan Las Baja Karbon Rendah Dengan Elektroda 6013. Jurnal Austenit, Vol 4(1).
Setyo dan Rendy. (2019). Pengaruh Kecepatan Pengelasan dan Jenis Elektroda Terhadap Kekuatan Tarik Hasil Pengelasan SMAW baja ST60. Jurnal Teknik Mesin Univ. Brawijaya Malang.
Tarkono, dkk. (2017). Studi Kekuatan Sambungan Las Baja AISI 1045 dengan Berbagai Metode Posisi Pengelasan. Jurnal Mekanikal.
Tarkono, Gabe Partinanda Siahaan, Zulhanif. (2018). Studi Penggunaan Jenis Elektroda Las Yang Berbeda Terhadap Sifat Mekanik Pengelasan SMAW Baja AISI 1045. Jurnal Mekanikal.
Santoso J., (2019). Pengaruh arus pengelasan terhadap kekuatan tarik dan ketangguhan las SMAW dengan elektroda E7018. Semanticscholar.