Identification of Glass Powder Effect for Filler Composition in Hot Roller Sheet "“ Wearing Course (HRS-WC) Mixture
DOI:
https://doi.org/10.26418/jts.v25i2.90456Keywords:
Glass Powder, Hot Roller Sheet Wearing Course (HRS-WC), AsphaltAbstract
This study examines the use of glass powder as a filler substitute in Hot Rolled Sheet"“Wearing Course (HRS-WC) asphalt mixtures to enhance performance and promote waste utilization. The research employed an experimental method following SNI and AASHTO standards, testing mixtures with 0%, 25%, 50%, 75%, and 100% glass powder substitution using the Marshall method. Results showed that 50% and 75% substitution levels produced the best performance in terms of stability and Marshall Quotient, while 100% substitution led to a decline due to the glass powder"™s inability to absorb asphalt. Increased glass powder content also reduced VIM values, indicating denser mixtures, although at 100% substitution, both VIM and VMA exceeded specification limits. The findings suggest that glass powder can be effectively used as a partial filler replacement, with optimal results achieved at 50"“75% substitution and 5"“7% asphalt content.References
Ahmed, T. A., & Williams, R. C. (2018). Using a modified asphalt bond strength test to investigate the properties of asphalt binders with poly ethylene wax-based warm mix asphalt additive. International Journal of Pavement Research and Technology, 11(1), 28-37.
Al-Taher, M. G., Sawan, A. M., Solyman, M. E. S. A., El-Sharkawi Attia, M. I., & Ibrahim, M. F. (2024). Evaluating the Durability of Asphalt Mixtures for Flexible Pavement Using Different Techniques: A Review. International Journal of Pavement Research and Technology, 1-27.
Almira, D. R., Puspasari, N., & Saputra, N. A. (2022). Pengaruh Penggunaan Serbuk Kaca Terhadap Karakteristik Marshall Campuran HRS-WC: The Effect Of The Use Of Glass Powder On The Characteristics Of Mixed Marshall HRS-WC. Media Ilmiah Teknik Sipil, 10(2), 78-84.
Enieb, M., Diab, A., & Yang, X. (2021). Short-and long-term properties of glass fiber reinforced asphalt mixtures. International Journal of Pavement Engineering, 22(1), 64-76.
Fabiani, V. A., Wahyuni, N., Brilliantoro, R., & Safitri, M. N. (2018). Sintesis Dan Karakterisasi Silika Gel Dari Limbah Kaca Serta Aplikasinya Pada Kromatografi Kolom. Indonesian Journal of Pure and Applied Chemistry, 1(1), 10-16.
Hidiyati, E. F., Cahyono, A. D., Induwati, M., Emilia, O. F., Mustafa, D. T., Pambudi, W. R., & Fasyaro, R. F. (2023). Identifikasi Karakteristik Agregat Terhadap Nilai Stabilitas Lapis Perkerasan Aspal Beton AC-BC (Laston). Teras Jurnal: Jurnal Teknik Sipil, 13(1), 193-206.
Jauhari, B., & Doda, N. (2019). Pengaruh gradasi agregat terhadap nilai karakteristik aspal beton (ac-bc). Gorontalo Journal of Infrastructure and Science Engineering, 2(1), 27-37.
Li, R., Xiao, F., Amirkhanian, S., You, Z., & Huang, J. (2017). Developments of nano materials and technologies on asphalt materials–A review. Construction and building materials, 143, 633-648.
Pradana, M. A., & Hartatik, N. (2023). Analisis Karakteristik Campuran Ac-Wc Menggunakan Aspal Polimer Dengan Metode Marshall Test. Jurnal Ilmiah Teknik dan Manajemen Industri, 3(2), 1079-1086.
Ridha, R., Syarwan, S., & Supardin, S. (2020). Pengaruh Substitusi Limbah Kaca Terhadap Pasir Pada Campuran Laston AC-BC. Jurnal Sipil Sains Terapan, 3(02).
Sugiyanto, G. (2017). Marshall test characteristics of asphalt concrete mixture with scrapped tire rubber as a fine aggregate. Jurnal Teknologi (Sciences & Engineering), 79(2).
Suherminanta, S., Palelu, A., Risdiyanto, R., & Kresnanto, N. C. (2022). Penggunaan Serbuk Kaca Sebagai Bahan Tambah/Filler pada Perkerasan Jenis HRS–WC Berdasarkan Karakteristik Marshall. RANCANG BANGUN TEKNIK SIPIL, 8(2), 44-53.
Sukarman, S. (2003). Beton Aspal Campuran Panas. Yayasan Obor Indonesia.
Susilowati, A., & Wiyono, E. (2019). Variasi Suhu Pemadatan Pada Campuran Beton Aspal Menggunakan Bahan Tambah Anti Stripping. Construction and Material Journal, 1(1), 12-20.
Swardana, R., Sari, Y. A., & Pamadi, M. (2022). Analisa Karakteristik Campuran Aspal Menggunakan Limbah Keramik. PILAR, 17(2), 67-73.
Triyatno, D., Cahyo, Y., & Ridwan, A. (2020). Meningkatkan Stabilitas Aspal Beton Dengan Menggunakan Filler Serbuk Kaca. Jurnal Manajemen Teknologi & Teknik Sipil, 3(1), 130-140.
Wang, C., Zhang, H., Castorena, C., Zhang, J., & Kim, Y. R. (2016). Identifying fatigue failure in asphalt binder time sweep tests. Construction and Building Materials, 121, 535-546.
Yang, K., Li, R., Yu, Y., Pei, J., & Liu, T. (2020). Evaluation of interlayer stability in asphalt pavements based on shear fatigue property. Construction and Building Materials, 258, 119628.
Yuniarti, R., Hasyim, H., Hariyadi, H., & Handayani, T. (2019). Penggunaan Limbah Kaca Sebagai Filler Pada Campuran Perkerasan Aspal Panas. J. Tek. Sipil, 26(3), 265.
Zhang, M., Hao, P., Dong, S., Li, Y., & Yuan, G. (2020). Asphalt binder micro-characterization and testing approaches: A review. Measurement, 151, 107255.
Downloads
Published
Issue
Section
License
Copyright (c) 2025 Jurnal Teknik Sipil
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.